符合GB/T 17493 T62 T1 1 C1 2C1M AWSA5.29 E91T1 B3C ISO 17634A T CrMo2 P C1 1

产品特性DESCRIPTION

SWE91B3产品为金红石型药芯焊丝，焊接过程为喷射过渡，具有焊接飞溅小，焊道平滑，熔覆效率高等特点。Mo的原子间结合力极强，所以在高温下仍有较好的强度，可以有效减少高温环境下的热变形并增加了焊道的耐腐蚀性。

The SWE91B3 product is a rutile-type flux-cored wire. Its welding process features spray transfer, with characteristics such as low welding spatter, smooth weld beads, and high deposition efficiency. Molybdenum (Mo) has extremely strong interatomic bonding force, so it maintains good strength even at high temperatures, which can effectively reduce thermal deformation in high-temperature environments and enhance the corrosion resistance of weld beads.

应用APPLICATIONS

适用于：15CrMoR 管件及ASTM SA387 钢材的焊接。

It is suitable for welding steels of 2.5%Cr～1%Mo, as well as ASTM A335-P22 and ASTM A387Gr.22.

电源类型CURRENT TYPE

焊枪接正电极DC+

过程保护PROCESS

100%Co2 Gas-shielded welding

焊接位置WELDING POSITIONS            

平焊、角焊、仰焊、立向上焊、立向下焊 Flat, fillet, tilt, vertical up , vertical down

熔敷金属化学成分CHEMICAL COMPOSITION OF WELDED METAL %

项目

C

Si

Mn

P

S

Cr

Mo

GB/T Standard

0.05-0.12

≤0.8

≤1.25

≤0.030

≤0.030

2.00-2.50

0.90-1.2

例值 Typical values

0.06

0.25

0.80

0.015

0.010

2.26

1.06

熔敷金属力学性能MECHANICAL PROPERTIES OF WELDED METAL

试验项目

Rel/Rp0.2屈服强度（MPa）

Rm抗拉强度（MPa）

A伸长率（%）

试验温度（℃）

KV2(J)

GB/T Standard

≥540

620-760

≥15

常温

-

例值 Typical values

600

730

20

90

焊后热处理Heat Treatment：（675-705）℃×（60-75）min

作业条件OPERATING CONDITIONS

直径Diameter [mm]

φ1.2

φ1.4

φ1.6

电流Current [A]

平焊Flat

150-300

180-320

200-400

上立焊/仰焊V-Up&Overhead

120-260

150-280

180-280

下立焊Vertical Downward

110-180

130-200

150-230

包装PACKAGING

5kg  15kg 盘装 Coil    也可以定制其他包装和规格Other packaging and other diameters: please consult us