符合GB T17853 TS410-F C1 1  AWSA5.22 E410T1-1 ISO  17633A T 13 P C1 1

产品特性DESCRIPTION

SW·E410主要成分为11-13 Cr，全焊缝金属显微组织几乎全为马氏体。 为了实现焊缝有足够的延展性，需要进行预热和焊后热处理。此类填充金属最常见的应用是焊接具有相似成分的合金。 它还用于在碳钢上沉积覆盖层以抵抗腐蚀、侵蚀或磨损。

SW·E410 has a main composition of 11-13% chromium (Cr), and the microstructure of the all-weld metal is almost entirely martensitic. In order to achieve sufficient ductility of the weld, preheating and post-weld heat treatment are required. The most common application of this type of filler metal is welding alloys with similar compositions. It is also used to deposit overlay on carbon steel to resist corrosion, erosion or abrasion.

应用APPLICATIONS

适用于焊接06Cr13等13Cr马氏体不锈钢，也可用于耐蚀、耐磨的表面堆焊。

It is suitable for welding 13Cr martensitic stainless steels such as 06Cr13. It can also be used for surface surfacing to achieve corrosion resistance and wear resistance.

电源类型CURRENT TYPE

焊枪接正电极DC+

过程保护PROCESS

100%CO2 Gas-shielded Welding

焊接位置WELDING POSITIONS            

平焊、角焊、仰焊、立向上焊、立向下焊 Flat, fillet, tilt, vertical up , vertical down

熔敷金属化学成分CHEMICAL COMPOSITION OF WELDED METAL %

项目

C

Si

Mn

P

S

Cu

Ni

Cr

Mo

GB/T Standard

≤0.12

≤1.00

≤1.2

≤0.040

≤0.030

≤0.75

≤0.6

11.0-13.5

≤0.75

例值 Typical values

0.038

0.45

0.45

0.024

0.004

0.035

0.04

11.8

0.05

熔敷金属力学性能MECHANICAL PROPERTIES OF WELDED METAL

试验项目

Rel/Rp0.2屈服强度（MPa）

Rm抗拉强度（MPa）

A伸长率（%）

试验温度（℃）

KV2(J)

GB/T Standard

≥390

490-670

≥18

-20

≥27

例值 Typical values

470

556

27

115

作业条件OPERATING CONDITIONS

直径Diameter [mm]

φ1.0

φ1.2

φ1.6

电流Current [A]

平焊Flat

120-200

140-220

200-300

上立焊/仰焊V-Up&Overhead

100-160

140-180

220-320

包装PACKAGING

5kg  12.5kg 盘装 Coil    也可以定制其他包装和规格Other packaging and other diameters: please consult us