符合GB T17853 TS410NiMo-F C1 1 AWS A5.22 E410NiMoT1-1 ISO 17633A T 13 4 P C1 1

产品特性DESCRIPTION

SW·E410NiMo主要成分为11-13 Cr，增加Ni、Mo耐蚀性更强，尤其提升了抗点蚀、缝隙腐蚀和耐还原性介质腐蚀的能力，可以应对更为复杂的腐蚀环境。为了实现焊缝有足够的延展性，需要进行预热和焊后热处理。

SW·E410NiMo has a main composition of 11-13% chromium (Cr), and the microstructure of the all-weld metal is almost entirely martensitic. To achieve sufficient ductility in the weld, preheating and post-weld heat treatment are required. The most common application of this type of filler metal is welding alloys with similar compositions. It is also used to deposit overlays on carbon steel to resist corrosion, erosion, or abrasion.

应用APPLICATIONS

适用于焊接04Cr13Ni5Mo、ASTMCA6NM钢，多用于焊接水轮机转子、阀门等耐磨耐腐蚀件。

It is suitable for welding 04Cr13Ni5Mo and ASTM CA6NM steels, and is mostly used for welding wear-resistant and corrosion-resistant components such as hydraulic turbine rotors and valves.

电源类型CURRENT TYPE

焊枪接正电极DC+

过程保护PROCESS

100%CO2 Gas-shielded Welding

焊接位置WELDING POSITIONS            

平焊、角焊、仰焊、立向上焊、立向下焊 Flat, fillet, tilt, vertical up , vertical down

熔敷金属化学成分CHEMICAL COMPOSITION OF WELDED METAL %

项目

C

Si

Mn

P

S

Cu

Ni

Cr

Mo

GB/T Standard

≤0.06

≤1.00

≤1.0

≤0.040

≤0.030

≤0.75

4.0-5.0

11.0-12.5

0.4-0.7

例值 Typical values

0.053

0.5

0.3

0.016

0.003

0.08

4.3

11.6

0.45

熔敷金属力学性能MECHANICAL PROPERTIES OF WELDED METAL

试验项目

Rel/Rp0.2屈服强度（MPa）

Rm抗拉强度（MPa）

A伸长率（%）

试验温度（℃）

KV2(J)

GB/T Standard

≥390

490-670

≥18

-20

≥27

例值 Typical values

470

556

27

115

作业条件OPERATING CONDITIONS

直径Diameter [mm]

φ1.0

φ1.2

φ1.6

电流Current [A]

平焊Flat

120-200

140-220

200-300

上立焊/仰焊V-Up&Overhead

100-160

140-180

220-320

包装PACKAGING

5kg  12.5kg 盘装 Coil    也可以定制其他包装和规格Other packaging and other diameters: please consult us