符合GB/T 5293 SU34 AWS A5.17 EH14 ISO 14171-B-SU33

产品特性DESCRIPTION

H10Mn2含有较高的锰含量，主要用于碳钢和低合金钢的焊接，特别是在需要较高强度的应用中。适合在在低温环境下强度要求更高的板材焊接。

H10Mn2 contains a relatively high manganese content and is mainly used for the welding of carbon steel and low-alloy steel, especially in applications requiring higher strength. It is suitable for the welding of plates that demand higher strength in low-temperature environments.

应用APPLICATIONS

与烧结型焊剂101配合，500MPa抗拉强度等级母材的高速焊接及填充焊接均可。具有非常稳定的熔敷金属机械性能。

When matched with sintered flux 101, it is suitable for both high-speed welding and fill welding of base metals with a tensile strength grade of 500MPa. It exhibits extremely stable mechanical properties of deposited metal.

电源类型CURRENT TYPE

焊枪接正电极DC+

过程保护PROCESS

配合SJ101焊剂 / SJ101 FLUX

焊接位置WELDING POSITIONS            

平焊、角焊Flat, fillet

熔敷金属化学成分CHEMICAL COMPOSITION OF WELDED METAL %

项目

C

Si

Mn

P

S

Cu

Ni

Cr

GB/T Standard

≤0.12

≤0.07

1.5-1.9

≤0.03

≤0.03

≤0.35

≤0.30

≤0.2

例值 Typical values

0.066

0.011

1.62

0.011

0.011

0.12

0.007

0.013

熔敷金属力学性能MECHANICAL PROPERTIES OF WELDED METAL

试验项目

Rel/Rp0.2屈服强度（MPa）

Rm抗拉强度（MPa）

A伸长率（%）

试验温度（℃）

KV2(J)

配合SJ101焊剂例值

≥390

490-670

≥18

-40

≥27

作业条件OPERATING CONDITIONS

直径Diameter [mm]

φ2.5

Φ3.2

Φ4.0

Φ5.0

电流Current [A]

平焊Flat

340～490

400～540

460～610

560～660

包装PACKAGING

25 kg      200 kg    250 kg 盘装 Coil    也可以定制其他包装和规格Other packaging and other diameters: please consult us